【摘 要】
：
Using L-glutathione (GSH) as a capping agent,ZnSe/GSH quantum dots (QDs) were prepared under microwave irradiation and irradiated under dark,ultraviolet light and incandescent light,respectively.The properties and interaction of different lights irradiate
【机 构】
：
The State Key Laboratory of Refractories and Metallurgy, Wuhan University of Science and Technology,
【出 处】
：
武汉理工大学学报（材料科学版）（英文版）
论文部分内容阅读
Using L-glutathione (GSH) as a capping agent,ZnSe/GSH quantum dots (QDs) were prepared under microwave irradiation and irradiated under dark,ultraviolet light and incandescent light,respectively.The properties and interaction of different lights irradiated ZnSe/GSH QDs and bovine serum albumin (BSA) were studied systematically.The fluorescence (FL) spectra results reveal that the quenching mechanism are all the static quenching in nature.The quenching constant (Ksv) and binding constant (K) value of different irradiated ZnSe/GSH QDs and BSA all increased with the change of light types from dark to incandescent light and UV light.The number of binding site (n) is close to 1 at different temperatures.The lighting types influence the enthalpy and entropy changes.The Fourier transform infrared (FTIR) spectra indicate that the light induced GSH ligand will facilitate photocatalytic oxidation on the surface of ZnSe/GSH QDs.The circular dichroism (CD) results show that the α-helicity content of BSA decreases from 60.34％,59.31％,to 58.79％ under UV lighting,incandescent lighting and dark conditions.The interaction results of different lights illuminated ZnSe/GSH QDs with BSA by CD spectra method matches well with that by FL and FTIR spectra.That is,the interaction of ZnSe/GSH QDs and BSA from strong to weak is UV light,incandescent light and dark in sequence.
其他文献
A new type of capric acid (CA)-acid expanded vermiculite (AEV) composite phase change material (PCM) with improved adsorption ability and interface adhesive strength was developed. Through the analysis of non-isothermal phase transition kinetics, modified
The isothermal absorption properties and kinetic model of Cr (Ⅵ) and Cr (Ⅲ) onto ettringite were investigated using the batch adsorption method. IR analysis was used to study the difference and mechanism of the adsorption of chromium ions with different v
The mechanical and thermal properties of steel reinforced concrete columns with CFRP reinforcement were examined after exposure to a high temperature of 500℃. The concrete made with normal and recycled coarse aggregate (RCA) was fabricated and three diffe
Due to the intrinsic nature of a heterogeneous and anisotropic microstructure of cement based materials and the small indentation size, the measured microhardness values are subject to considerable variability. This work presents an in-depth assessment of
Cement raw meal with MSS and different heavy metals was blended to examine the fixation ratios, chemical species, and cement crystalline phases in clinkers. The results showed that blending MSS could decrease the fixation ratio of Cr, Ni, Cu, and Zn in th
Hydration heat behavior and kinetics of blended cement containing up to 20％ MSWI fly ash were investigated based on its hydration heat evolution rate measured by isothermal calorimeter. Kinetics parameters, N and K, and hydration degree, Ca(OH)2 content,
Pure copper plates were coated by Ni-TiC dipulse current plating method.The effects of adding different concentration(ranging from 0.5 g/L to 3.0 g/L) of attapulgite nano particles to the plating bath on the surface morphology,wear resistance,and oxidatio
The elastic-plastic transition regime and brittle-ductile transition regime in scratch process for optical glass BK7 were analyzed based on the Hertzian equation and the stress ratio theory which was proposed by Wei. The interacting scratch process for op
Four cellulose ethers (CEs) were compared for their effects on the pore structure of cement paste using mercury intrusion porosimetry. The experimental results show that the total pore volume and porosity of cement pastes containing the four cellulose eth
The Ni nanoparticles coated with Pb(Zr,Ti)O3 (PZT) were synthesized by a sol-gel method and in situ reaction. And their structure, oxidation resistance, and electromagnetic properties were investigated. The X-ray diffraction patterns (XRD) exhibited that